UNS S13800(XM-13, 13-8Mo)
Precipitation-hardening stainless steel UNS S13800

UNS S13800Equal material : XM-13, 13-8Mo

UNS S13800stainless steel description:
UNS S13800stainless steel is a kind of precipitation stainless steel, aluminum content is higher, the steel after solid solution treatment the hardness value is not more than 38HRC for cutting. After 510 degree, precipitation hardening, hardness greater than 45HRC, the comprehensive mechanical properties can be obtained strong.

UNS S13800stainless steel mechanical properties :
Thickness of the steel heat treatment of /mm ó 0.2/MPa ó b/MPa δ (% HRC) hardness0.10~ < 8 solid solution treatment ≤ 380.10~ < 0.50 (510 ± 6) and (510 ± 6) degree precipitation hardening ≥ 1410 ≥ 1515 ≥ 6 ≥ 450.50~ < 5 > 85.0~8.0 10
UNS S13800stainless steel physical property:
Solid solution temperature of 1020~1100 degree, water-cooled, hardness ≤ 38HRC.
UNS S13800 stainles steel common product exciting form: stainless steel plates, stainless steel sheet, stainless steel bar, stainless steel tube.
UNS S13800stainless steel application:
UNS S13800stainless steel is mainly used in the manufacture of high precision and high wear resistance, corrosion resistant parts.
Key words: UNS S13800 stock, UNS S13800 competitive price, UNS S13800 high quality, UNS S13800 supplier, UNS S13800 manufacturer.                        
 http://www.steel-jw.com
 http://www.steel-plates.com
vivian@steel-jw.com
Skype: vivian@steel-jw.com
Tel 86, 371, 63332179